Journal of the Chilean Chemical Society

versión On-line ISSN 0717-9707

J. Chil. Chem. Soc. vol.62 no.2 Concepción jun. 2017 





a) Universidad de Santiago de Chile, Facultad de Química y Biología, Departamento de Química de Los Materiales, Avenida B. O'Higgins 3363, Estación Central, Santiago, C.P. 9170022, Chile.
Centro de Investigación de Procesos Redox (CiPRex) and Advanced Center for Chronic Diseases (ACCDiS), Facultad de Ciencias Químicas y Farmacéuticas, Universidad de Chile, Santiago, Chile.
* e-mail:;


Hydrogen peroxide (H2O2) plays an important role as an intermediary in different biological, chemical and environmental systems. It has been widely used as an oxidizing and antimicrobial agent, in germicides production and textile and paper bleaching. However, it is well known, that H2O2 is a possible responsible in many diseases and is a chemical agent that threatens the environment, so it becomes important to detect peroxide with high accuracy. In this study, carbon paste electrode (CPE), modified with Co2SnO4 was synthesized and tested. It was successfully obtained a non-enzymatic H2O2 detection type sensor, based on Co2SnO4/ CPE composite, showing good linear response in concentration of H2O2 in the range of 88 - 605.9 μM.

Keywords: Hydrogen peroxide, Carbon paste electrode, Co2SnO4



Hydrogen peroxide (H2O2) plays an important role as an intermediary in different biological, chemical and environmental systems. It has been widely used as an oxidizing and antimicrobial agent, in germicides production and textile and paper bleaching [1,2]. However, it is well known, that H2O2 is a possible responsible in many diseases and is a chemical agent that threatens the environment, so it becomes important to detect peroxide with high accuracy [3]. For the chemical determination of H2O2 it is usually used methods such as volumetric analysis [4], spectrophotometry [5], fluorescence [6], electrochemistry [7] and chromatography [8]. In particular, several electrochemical methods have been reported as sensors for detecting H2O2 because they are a high sensitivity alternative at low cost and easy operation [7]. Recently, many biosensors have been studied as H2O2 detectors, such as enzymes/proteins immobilized in different materials, such as hemoglobin, carbon nanotubes, cytochrome C, etc. [9, 10, 11]. However the applications of these biosensors are restricted, because immobilization processes are complicated and activity is drastically affected by external factors such as temperature, humidity and pH [7, 12]. In this regard, it is important to develop non-enzymatic H2O2 sensors, presenting high sensitivity, stability, hardiness, economical and easy preparation. In this context, metal oxides (Fe3O4, V2O5, NiO, SnO2, MnO2, etc.), metal compounds such as ternary MCo2O4 (M = Zn, Ni, etc.), MFe2O4 (M = Ni, Mn, etc.), nanocomposites of PDAG/reduced graphene oxides (GRO) [13] and recently, electroceramic oxide composite such as Co2SnO4/ graphene have been considered as promising candidates for H2O2 detection[14]. Co2SnO4, is frequently used as conductive electrode in lithium ion batteries and as supercapacitor because of its electrical properties [15-16].

In this study, Co2SnO4/CPE electrode was prepared and tested. It was successfully obtained a non-enzymatic H2O2 detection type sensor. Co2SnO4/ CPE composite showed good linear response in concentration of H2O2 in the range of 88 - 605.9 μM.



All chemicals were of analytical grade from Merck. Mineral oil was purchased from Sigma and sodium chloride and hydrochloric acid were from J.T Baker. Hydrogen peroxide was from Merck, 30%. The H2O2 standard solution was standardized by KMnO4 0.2N which was previously standardized by Na2C2O4. A stock solution of 29.4 mM H2O2 was prepared by 30% H2O2 solution and diluted with deionized and bidistilled water. 0.5M NaCl as the electrolyte and drops of concentrated HCl and NaOH were used to change the pH of the solution.


X-ray diffraction (XRD) measurements were performed using a MTI diffractometer, model MD-10 with a Cu radiation source (kα1/α2) = 1.54178 Å λ in a range of 2Θ = 15 - 70. The analysis of crystalline phases was performed using the Crystal Impact Match program with PDF-2 database. Parameter lattices were calculated using the STOE XPOW software. Morphological characterization was carried out in a scanning electron microscope (SEM), TESCAN, Vega 3 model. Compositional study was conducted by analysis of energy dispersive spectroscopy (EDS) using a Bruker probe, model QUANTAX 400a series. To perform electrochemical measurements 900B CH Instruments potentiostat was used at room temperature (25 ± 2 °C).

Electrochemical experiments: a conventional three electrode cell was employed where the working electrode is the composite electrode (Teflon tubes with a metal connection were used for making working electrodes, Teflon hollow electrodes of geometrical area 0.031 cm2), Ag/AgCl (3M KCl) reference electrode, and a platinum wire was the counter electrode. Before each experiment, the working electrodes were polished and washed with deionized and double distilled water and cycled in the electrolyte solution 0.5M NaCl until a stable voltammetric response was obtained.

Electrode modification: The modification was performed by direct mixing 10% electroceramic oxide with 60% graphite and 30% of mineral oil by weight in an agate mortar. Then, it was added 10 mL of diethyl ether for homogenizing until solvent evaporation [17-18].

Cyclic voltammetry (CV): For electrochemical characterization carbon paste electrode (CPE) and Co2SnO4/CPE were measured in a potential range of -0.8V to 0.6 V at a scan rate of 0.05 V/s in a 0.5M NaCl solution which was previously purged with N2 for 20 minutes.

Amperometry: In the electrochemical cell with electrolyte solution 0.5M NaCl (and drops of NaOH) pH = 10.2, aliquots of a standard solution of 29.4 mM H2O2 were added every 150 s for a total time 1300 s. Measurements were performed at a potential of -0.27 V.


Synthesis of Co2SnO4

For the synthesis it was mixed CoO and SnO2 in molar ratio 2: 1 in agate mortar. Acetone was added until a smooth paste is formed. Finally the resulting mixture was calcined in a furnace at 1000 °C for 24 h for obtaining ceramic oxide particles [14].

The reactions is described as follows (eq. 1)

Structural characterization

X-ray diffraction (XRD)

Ceramic oxide Co2SnO4 corresponds to a spinel structure with Fd3m space group. The structural formula that defines the distribution of the cations in a normal and reverse spinel is (eq. 4):

Where IV corresponds to tetrahedral sites and VI to octahedral sites. At low temperatures, when T → 0K and X → 0, the structure correspond to a normal spinel, namely all atoms A occupy tetrahedral sites and B are located in octahedral sites. When X → 1 the spinel becomes an inverse spinel. This is the specific case of the Co2SnO4 ceramic oxide. In this case a new spatial distribution of cations A and B takes place. A percentage of cation A is occupying tetrahedral sites and the other percentage of A and B are in octahedral sites [19-20]. Figure 1 shows the diffraction pattern of Co2SnO4.


Figure 1: XRD Pattern of Co2SnO4


Figure 1a shows that XRD pattern of the synthesized material compared with the data base correspond to Co2SnO4, crystallizing in the Fd3m space group and a calculated cell parameter of 8.847 A°. There are no secondary phases or evidence of unreacted raw materials assuring a pure crystalline phase.

Scanning electron microscopy (SEM)

Figure 2 shows morphology of Co2SnO4 In this case, it can be observed a granular grain morphology and an average grain size of 0.57 μm.


Figure 2: Scanning electron microscopy (SEM)
of Co2SnO4


Modified electrodes

The modified electrodes were tested using the ferri-ferrocyanide redox couple. A solution of potassium hexacyanoferrate was dissolved in 0.5 M NaCl and the response was recorded at a scan rate of 50 mV/s. The electroactive area was determined using the Randles -Sevcik equation [21] (eq.3).

Where D is the parameter of diffusional coefficient of the species Fe (II) (7,610-6 cm2/s) [21], n is the number of electrons transferred (n=1), C is the concentration of Fe (II)/Fe (III) (2 mM), v is the scan rate (50 mV/s). The geometric area measured for the CPE electrode was 0.031 cm2. Table 1 summarizes the electroactive area values calculated according to equation 5. The relative roughness factor (R = electroactive area area/geometrical area) and AE of the couple Fe (II)/Fe (III) for composites electrodes and CPE are also summarized.


Table 1: Electroactive area, relative roughness factor
and ΔE for composites electrodes and CPE.


Electrochemical characterization of the electrodes in the presence of H2O2 Cyclic voltammetry

The redox behavior of the composite and CPE were studied by cyclic voltammetry. Fig. 3 shows the cyclic voltammograms of the composite and CPE in 0.5M NaCl solution (pH=10.2) in the presence of H2O2. It is interesting that the modified electrode showed high activity compared to the CPE shifting the potential and increasing the current density. When comparing CPE vs. Co2SnO4/CPE system shows that H2O2 does not present redox peak but instead a current discharge at the bare CPE electrode. In contrast, the composite Co2SnO4/CPE shows a redox peak at -0.22 V.


Figure 3: Cyclic voltammetry profiles of composite
electrodes and CPE in the presence of 48.9 mM H2O2
0.5 M NaCl at pH=10.2. Scan rate: 0.05 V/s. a) (thin line)
CPE, (bold line) Co2SnO4/CPE


Figure 4 shows cyclic voltammetry responses of CPE/Co2SnO4 when changing the concentration of H2O2. It can be seen that increasing the H2O2 concentration, the reduction current increases, suggesting that this electrode has an amperometric sensor behavior.


Figure 4: Cyclic voltammetry responses of composite electrode
Co2SnO4/ CPE at growing concentrations of H2O2 in solution of
0.5 M NaCl at pH=10.2 (see the arrow). Scan rate: 0.05 V/s.



The amperometric study of the reduction of hydrogen peroxide with Co2SnO4/CPE composite electrode was performed adding aliquots of 30 μL 29.4 mM H2O2 to 10 mL of solution each 150 s during 1300 s applying a constant potential -0.27 V.

Figure 5a shows the amperometric response of the Co2SnO4/CPE composite electrode in the presence of increasing concentrations of H2O2 concentration from 88.0 to 605.0 μM. It can be seen that the current signal increases when concentration increases, showing a linear correlation (R = 0.9888), indicating that this composite electrode can be used as amperometric sensor for H2O2 (see figure 5b). The calibration curve of J Vs C shows the following analytical parameters: detection limit (μM)= 65.38, sensitivity (μAcm2/μM) = 3,81x10-8, linear range [88 - 605,9 μM].


Figure 5: a) J Vs t response of the CPE/Co2SnO4 composite when adding aliquots of 30 μL
29.4 mM of H2O2 each 150 s. b) Calibration curve for the Co2SnO4/ CPE composite electrode
between 88 μm - 605.9 μm of H2O2 in 0.5M NaCl at pH=10.2.


Table 2 compares different sensors for peroxide showing that the composite electrode is cheap, stable, has good sensitivity and can be used easily for the detection of H2O2 in the range of linearity 88 μM - 605 μM


Table 2: Comparison of different sensors for detecting H2O2

* rGO: Reduced graphene oxide, GO: Graphene oxide NPs:
Nanoparticles, HRP: Horseradish peroxidase; GCE: Glassy
carbon electrode



It was obtained a stable, low cost, amperometric electrode sensor for hydrogen peroxide using a carbon paste electrode modified with Co2SnO4 ceramic compound.


FONDECYT 1160324, FONDECYT 1161225, Dicyt-USACH and Project RC 130006, CILIS, granted by Fondo de Innovación para la Competitividad, del Ministerio de Economía, Fomento y Turismo, Chile,



1.- R. Chaisuksant, T. Chomsook, N. Manthong, K. Kalcher, low cost Hydrogen peroxide sensor from manganese oxides modified pencil graphite electrode, 20, 81-84 (2016).

2.- M. Darder, K. Takada, F. Pariente, E. Lorenzo, H.D. Abruna; Dithiobissiccinidyl propionate as an anchor for assembling peroxidases at electrodes surfaces and its application in a H2O2 biosensor, 71, 5530-5537 (1999)

3.- P. Kovacic, A Proposed Role for Hydrogen Peroxide in Carcinogenesis, 60, [5], 283-290 (1960).

4.- N. Klassen, D. Marchington, H. McGovan, H2O2 determination by the I3- method and by KMnO4 titration, 66, 2921-2925 (1994) .

5.- C. Chih Hsu,Y. Rong Lo,Y. Chian Lin, Y. Cen Shi, P. Lung Li A Spectrometric Method for Hydrogen Peroxide Concentration Measurement with a Reusable and Cost-Efficient Sensor,15, [10], 25716-25729 (2015).

6.- N Burmistrovaa, R. Meier , S. Schreml , A. Duerkop, Reusable Optical Sensing Microplate for Hydrogen Peroxide Using a Fluorescent 2 Photoinduced Electron Transfer Probe (HP Green), 193, 799-805 (2014)

7.- H. Pang, F. Gao, Q. Chen, R. Liu, Q. Liu, Dendrite-like Co3O4 nanostructure and its applications in sensors, supercapacitors and catalysis, 41, 5862 - 5868 (2012)

8.- U. Pinkernell , S. Effkemann, U. Karst, Simultaneous HPLC Determination of Peroxyacetic Acid and Hydrogen Peroxide, 69 , [17], 3623-3627 (1997)

9.- A. Saleh, Hydrogen Peroxide Biosensors Based on Horseradish Peroxidase and Hemoglobin, 55, 1-11 (2013)

10.- F. Tian, B. Xu, L. Zhu, G. Zhu, Hydrogen peroxide biosensor with enzyme entrapped within electrodeposited polypyrrole based on mediated sol-gel derived composite carbon electrode, 443, [1], 9-16 (2001)

11.- A. Uzunoglu, S. Song, L. Stanciua, A Sensitive Electrochemical H2O2 Sensor Based on PdAg-Decorated Reduced Graphene Oxide Nanocomposites, 163 [7] B379-B384 (2016).

12.- E. Reitz, W. Jia, M. Gentile, Y. Wang, Y. Lei, CuO Nanospheres Based Nonenzymatic Glucose Sensor, 20, 2482-2486 (2008).

13.- S. Asim, S. Bahadar, A. Asiri; Electrochemical sensor for H2O2 using a glassy carbon electrode modified with a nanocomposite consisting of graphene oxide, cobalt(III) oxide, horseradish peroxidase and nafion, DoI: 10.1007/s00604-016-1942-0 (2016).

14.- Co-doped stannates /reduced graphene composites: Effect of cobalt substitution on the electrochemical sensing of hydrogen peroxide, Sensors and Actuators B: Chemical, 250, 412-419 (2017).

15.- Bonan An, Qiang Ru, Shejun Hu, Xiong Song, Juan Li; Facile synthesis and electrochemical performance of Co2SnO4/Co3O4 nanocomposite for lithium-ion batteries; Materials Research Bulletin; 60, 640-647 (2014).

16.- Chang Chen, Qiang Ru, Shejun Hy, Bonan An, Xiong Song, Xianhua Hou; Co2SnO4 nanocrystals anchored on graphene sheets as high-performance electrodes for lithium-ion batteries; Electrochimical Acta 151; 203-213 (2015).

17.- K. Kalcher, Chemically Modified Carbon Paste Electrodes in Voltammetric Analysis; 2, 419-433 (1990).

18.- Sensor based on carbon paste in electrochemycal analysis: A review with particular emphasis on the period 1990-1993. Kalcher*, K., Kauffmann, J., & Wang, J.; Electroanalysis, 7, [1], 5-21 (1995).

19.- J. Amilcar; Sintetización e incorporación de la fase Co2SnO4 en varistores cerámicos basados en SnO2 Universidad Autónoma de Nuevo León, Facultad de Ingeniería Mecánica y Eléctrica; Tesis Grado de Doctor (2013).

20.- A. Navrotsky, O. Kleppa; The thermodynamic of catión distributions in simple spinels, Journal of Inorganic and nuclear Chemistry; 2701-2714 (1967).

21.- F. Fuenzalida; Electrodos de pasta de carbono modificados con liquidos ionicos derivados del hexafluorfosfato de N-Octilpiridinio: Efecto del sustituyente en electrocatálisis; Universidad Santiago de Chile, Facultad Quimica y Biologia; Tesis doctoral (2015).

22.- Y. Zhang, Z. Wang, Y. Ji, S. Liu, T. Zhang, Synthesis of Ag nanoparticle-carbon nanotube-reduced graphene oxide hybrids for highly sensitive non-enzymatic hydrogen peroxide detection; 5, 39037-39041 (2015).

23.- Y. Ye, T. Kong, X. Yu, Y. Wu, K. Zhang, X. Wang; Enhanced nonenzymatic hydrogen peroxide sensing with reduced grapheneoxide/ ferroferric oxide nanocomposites; 89; 417 - 421 (2012).

24.- F. Xu, M. Deng, G. Li, S. Chen, L. Wang; Electrochemical behavior of cuprous oxide-reduced graphene oxide nanocomposites and their application in nonenzymatic hydrogen peroxide sensing; 88; 59 - 65 (2013).


Creative Commons License Todo el contenido de esta revista, excepto dónde está identificado, está bajo una Licencia Creative Commons