SciELO - Scientific Electronic Library Online

 
vol.26 número3Algoritmo RMLSA para redes ópticas flexibles en operación dinámicaCaracterización microestructural y mecánica de aceros de fase dual (ferrita-martensita), obtenidos mediante procesos térmicos y termomecánicos índice de autoresíndice de materiabúsqueda de artículos
Home Pagelista alfabética de revistas  

Servicios Personalizados

Revista

Articulo

Indicadores

Links relacionados

  • En proceso de indezaciónCitado por Google
  • No hay articulos similaresSimilares en SciELO
  • En proceso de indezaciónSimilares en Google

Compartir


Ingeniare. Revista chilena de ingeniería

versión On-line ISSN 0718-3305

Resumen

J. RODRIGUEZ, Rafael; A. CABALLIS, Carlos; CELY B., María Mercedes  y  UNFRIED-SILGADO, Jimy. A comparative study of corrosión resistance in welded joints of aluminium alloy AA1100 obtained by friction-stir and Gas Metal arc welding processes. Ingeniare. Rev. chil. ing. [online]. 2018, vol.26, n.3, pp.419-429. ISSN 0718-3305.  http://dx.doi.org/10.4067/S0718-33052018000300419.

In this study was evaluated the corrosion behavior of welded joints obtained by electric arc and friction stir welding in AA1100 aluminum alloy with the aim to compare the effects of the process on the corrosion resistance. Tests were performed on salt spray chamber andpotentiodynamic polarization test on welded joints based on ASTM B117 and ASTM G5 standards, respectively, using NaCl. The corrosion rate, mass loss behavior and potentiodynamic curves were analyzed. The analyzes were complemented by observation of tested surfaces with stereology and scanning electron microscopy. The results showed that localized corrosion was observed in both processes, which was stronger in the fusion region of welding arc processed samples. Furthermore, this last kind of samples showed higher mass loss and higher corrosion rate than the solid state processed samples.

Palabras clave : Aluminium alloys; welding; corrosion; potentiodynamic test.