SciELO - Scientific Electronic Library Online

 
vol.22 número4Evaluation of Pleurotus ostreatus basidiomes production on Pinus sawdust and other agricultural and forestry wastes from patagonia, ArgentinaEconomic profitability of particleboards production with a diversified raw material structure índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Maderas. Ciencia y tecnología

versão On-line ISSN 0718-221X

Resumo

LIMA, Adauto José Miranda de; IWAKIRI, Setsuo  e  TRIANOSKI, Rosilani. Determination of the physical and mechanical properties of wood-cement boards produced with Pinus spp and pozzolans waste. Maderas, Cienc. tecnol. [online]. 2020, vol.22, n.4, pp.527-536. ISSN 0718-221X.  http://dx.doi.org/10.4067/S0718-221X2020005000411.

The objective of this research was to evaluate the physical-mechanical properties of wood-cement boards produced with waste particles of Pinus spp. and sufficient levels of pozzolans to assimilate all Ca(OH)2 produced during the hydration reactions of Portland cement. The pozzolans used were: silica fume, metakaolin, rice husk ash, and calcined ceramic waste. The values of the pozzolans were determined based on the theoretical determination of the Ca(OH)2 content produced by the hydration reactions of Portland cement. The pozzolanic activity index was determined by the modified Chapelle test. The boards were produced through cold compression, and the test specimens were produced and tested for physical and mechanical properties at 28/91 days of curing. The minimum values employed in the Bison® commercial process were used as a reference for the physical-mechanical characterization. The boards produced presented good physical-mechanical properties even with high levels of replacement of cement by pozzolans. These properties were similar to the ones presented by the reference boards, despite the significant reduction in the specific mass of the prototype boards, which demonstrates the technological possibility of the use of these materials in the production of wood-cement boards.

Palavras-chave : Wood-cement boards; Pinus spp; silica fume; metakaolin; rice husk ash; calcined ceramic waste..