SciELO - Scientific Electronic Library Online

 
vol.22 número4Estimation model of mechanical properties from the compressive strength valuesUptake of insecticides and fungicides by impregnable and refractory coniferous wood species treated with commercial bio-based emulsion gel formulations índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Maderas. Ciencia y tecnología

versão On-line ISSN 0718-221X

Resumo

DE OLIVEIRA, Rafael G. E. et al. Analysis of glue line and correlations between density and anatomical characteristics of Eucalyptus grandis × Eucalyptus urophylla glulam. Maderas, Cienc. tecnol. [online]. 2020, vol.22, n.4, pp.495-504. ISSN 0718-221X.  http://dx.doi.org/10.4067/S0718-221X2020005000408.

This study aimed to analyze the glue line thickness effect and its relation with the density and anatomical characteristics of eucalyptus wood. Thus, the thickness of main and secondary glue lines was measured as well as their interaction with the apparent density of elements glued with resorcinol-formaldehyde (RF) and castor oil polyurethane (CP) adhesives. Anatomical wood characterization of Eucalyptus grandis × Eucalyptus urophylla was performed by correlating glue line thickness. According to normative instruction, specimens were produced for delamination tests. The experiment was conducted in a completely random 2 × 2 design factorial scheme (two classes of wood apparent density and two adhesives). Pearson correlation (t < 0,01) was performed among variables. It was found that there was adhesive penetration into vessels and rays of wood. Glue line thickness was higher in woods with density higher than to 580 kg/m3 glued with RF adhesive. There was a low correlation between wood density and vessel diameter to main and secondary glue lines (t < 0,01).

Palavras-chave : Apparent density; castor polyurethane; delamination; laminated wood; resorcinol-formaldehyde..