  REVISTA FACULTAD DE INGENIERÍA, U.T.A. (CHILE), VOL. 11 Nº1, 2003, pp. 65-69

MEDICIÓN DE LAS FUERZAS DE CORTE CON UN DINAMÓMETRO PIEZO ELÉCTRICO DURANTE EL TALADRADO TÉRMICO POR FLUENCIA 1

Juan Godoy R.2     Jorge Vergara D.2     Jaime Villanueva A.2
Martín Quispe Y.2     Percy Oviedo O.2     Franz Tikal3     Stefan Damm3

[1] Universidad de Tarapacá, Laboratorio de Procesos de Manufactura, Dpto. de Mecánica, Arica - Chile

[2] Universidad de Tarapacá, Dpto. Mecánica, Casilla 6-D, Arica-Chile, jmgodoy@uta.cl, jvergara@uta.cl, jvillanu@uta.cl

[3] Universidad de Kassel, Instituto de Producción y Logística, Alemania


RESUMEN

A través de una cooperación internacional con la Universidad de Kassel de Alemania, se desarrolló un proyecto conjunto para determinar las fuerzas de avance y momento torsor en chapas de cobre y latón en el proceso de taladrado por fluencia térmica (TFT). En el Laboratorio de Procesos de Manufactura de la Universidad de Tarapacá fue instalado un equipo para medir fuerzas y momentos, conectado a un PC mediante una tarjeta de adquisición de datos. Mediante el software XACT, se obtuvieron las curvas de la fuerza de avance Fz y el momento torsor Mz, generadas durante el proceso.

Inicialmente con masas patrones y una llave de torque, se calibró el dinamómetro. Posteriormente se hicieron mediciones en las láminas de cobre y latón. Se concluyó que las fuerzas de avance y momentos torsores son mayores en chapas de latón cuando son comparadas con las chapas de cobre, para un mismo espesor.

Keywords: Procesos de manufactura, mediciones, taladrado no convencional, láminas de cobre

ABSTRACT

Through an international cooperation with the University of Kassel, Germany a research project was developed for studying the cutting forces components and momentum determination in thin Copper and Brass sheets during the Thermal Flow Drilling (TFD) processes. In the Manufacturing Processes Laboratory of the Mechanicals Emgineering Department of Universidad de Tarapacá, Arica, Chile, equipment for measuring forces and torque measurements was installed. It was connected to a data card and installed in a pc bus. With the AXACT software it was possible to develop the feed force component and momentum or torque curves.

Initially, with standard mass and a torque wrench the equipment was calibrated. After this, feed force and torque measurements were made in those thin Copper and Brass sheets. As a conclusion the feed force and the torque momentum were bigger for Brass than Copper sheets of the same thickness.

Keywords:Manufacture process, measurements, non-conventional drilling, copper sheet


AGRADECIMIENTOS

Se agradece a CONICYT - DAAD, proyecto ALECHILE, a la Universidad de Kassel de Alemania y Universidad de Tarapacá - Chile, por haber financiado el proyecto "Taladrado Térmico por Fluencia en Láminas delgadas."

A la empresa FLOWDRILL B. V. de Holanda.

REFERENCIAS

[1] T. Novosel; "Tapping without chips. American Machinist", p.p. 103-105, Oct.1975.         [ Links ]

[2] G. Kretschmer, Flieblochformer Von Blechdurchzügen. U. Siegen, Doctoral Tesis Maschinenbau - Universität Gesamthochschule - Siegen 1980.         [ Links ]

[3] J. C. Oliveira L.; Maestría "Taladrado por fluencia y Roscado por Conformación", Universidad de Santa Catarina, Brasil, Florianopolis, abril 1994.         [ Links ]

[4] W. Weingaertner.; Revista Máquinas e Metais, Nº 368, p.p. 85-97, septiembre 1996.         [ Links ]

[5] J. C. Oliveira L.; Tesis de Doctorado "Una colaboración para la continuidad del desarrollo de la tecnología del Taladrado por Fluencia", Universidad de Kassel. Alemania, 1999.         [ Links ]


Recibido el 13 de junio de 2003, aceptada el 19 de agosto de 2003.