SciELO - Scientific Electronic Library Online

 
vol.10 número1Eficacia de la Azitromicina asociada al raspado y alisado radicular en periodontitis crónicaRelación entre frenillos labiales y periodonto en una población peruana índice de autoresíndice de assuntospesquisa de artigos
Home Pagelista alfabética de periódicos  

Serviços Personalizados

Journal

Artigo

Indicadores

Links relacionados

  • Em processo de indexaçãoCitado por Google
  • Não possue artigos similaresSimilares em SciELO
  • Em processo de indexaçãoSimilares em Google

Compartilhar


Revista clínica de periodoncia, implantología y rehabilitación oral

versão On-line ISSN 0719-0107

Resumo

BERSEZIO, Cristian et al. Influence of the Passive Evaporation of adhesive on the conductance of dentin. Rev. Clin. Periodoncia Implantol. Rehabil. Oral [online]. 2017, vol.10, n.1, pp.38-40. ISSN 0719-0107.  http://dx.doi.org/10.4067/S0719-01072017000100038.

Aim:

Determine the influence of time of passive evaporation of the solvent in a universal adhesive on the hydraulic conductance and permeability of dentin in an ex vivo human model. Henceforth, 60 healthy non-occluding third molars, indicated for therapeutic extraction/removal, of informed and consented patients aged between 18 and 30 years, were used here in. First, extracted teeth were incorporated into epoxy resin blocks and then dentin disks (1mm +/- 0.1 mm thick) were prepared. Dentin was acid etched with 35% ortho-phosphoric acid for 15 seconds in order to remove the smear layer and obtain permeable dentin. Samples were then randomized and divided into 5 groups (n=12). A Single Bond Universal adhesive layer with different time of passive evaporation of the solvent was then applied: GC=10 seconds, G1=30 seconds, G2=60 seconds, G3=300 seconds and G4=50 minutes. Finally, the flow rate was measured using a diffusion chamber, a model previously proposed by Pashley et al.

Results:

The obtained hydraulic conductance averages were as follows: GC=0.00052, G1=0.00018, G2=0.00006, G3=0.00005, G4=0.00005 expressed in uL•cm-2•min-1cm•H2O-1. For comparisons between groups, ANOVA and post hoc Tukey (ρ<0.05) tests were applied, resulting in a statistically significant difference between the GC group and all experimental groups (ρ <0.05). An influence of solvent passive evaporation thereby reducing hydraulic conductance in the experimental groups, was detected.

Palavras-chave : Passive evaporation; adhesion; hydraulic conductance.